Resonator for thermo optic device

ABSTRACT

A resonator for thermo optic devices is formed in the same process steps as a waveguide and is formed in a depression of a lower cladding while the waveguide is formed on a surface of the lower cladding. Since upper surfaces of the resonator and waveguide are substantially coplanar, the aspect ratio, as between the waveguide and resonator in an area where the waveguide and resonator front one another, decreases thereby increasing the bandwidth of the resonator. The depression is formed by photomasking and etching the lower cladding before forming the resonator and waveguide. Pluralities of resonators are also taught that are formed in a plurality of depressions of the lower cladding. To decrease resonator bandwidth, waveguide(s) are formed in the depression(s) of the lower cladding while the resonator is formed on the surface. Thermo optic devices formed with these resonators are also taught.

FIELD OF THE INVENTION

[0001] The present invention relates to thermo optic devices, such as optical waveguides. In particular, it relates to a resonator for frequency coupling between input and output waveguides of a thermo optic device. Even more particularly, it relates to an efficiently formed resonator having increased bandwidth.

BACKGROUND OF THE INVENTION

[0002] The art of making and developing new uses for thermo optic devices continues to emerge. Presently, thermo optic devices are used as filters, switches, multiplexers, waveguides, and a host of other semiconductor and optical transmission devices.

[0003] With reference to FIGS. 1A and 1B, a prior art thermo optic device in the form of an optical waveguide is shown generally as 110. It comprises a grating 112 formed of a lower cladding 114, an upper cladding 116, an input waveguide 118, an output waveguide 120 and a resonator 122. As is known, the waveguides and resonator are formed of a material having a higher or lower refractive index than that of the upper and lower claddings to propagate light in the resonator and waveguides during use. The grating 112 is disposed on a substrate 124. In many thermo optic devices the substrate is a printed circuit board or some form of silicon.

[0004] In forming the device, the lower cladding is deposited on the substrate. An intermediate layer, for the waveguides and resonator, is deposited on the lower cladding, photo patterned and etched. The upper cladding is deposited on the waveguides and resonator. In an alternate formation process, the lower cladding 206 is an oxidation of a silicon substrate with the waveguides, resonator and upper cladding being formed in the same manner.

[0005] The inherent characteristics of a resonator, such as its size, shape, composition, etc., may vary greatly from resonator to resonator as a function of the particular application in which the thermo optic device is to be used. The characteristics of all resonators, however, are generally selected in such a manner to eliminate crosstalk between the input and output waveguides at undesirable frequencies and to resonate signals (i.e., prolong and/or intensify) at desirable frequencies. These desirable frequencies are typically defined in a bandwidth of some length about a center frequency.

[0006] In the representative prior art embodiment shown in FIG. 1B, the resonator 122 has a generally symmetrical tooth-shaped pattern. To set the center frequency, the pitch between teeth is adjusted.

[0007] To set the bandwidth, an aspect ratio is adjusted in an area where the waveguide and resonator front or face one another. For example, in FIG. 1A, resonator 122 has a surface 123 facing a surface 119 of input waveguide 118. The aspect ratio (a.r.) in this area is defined as the area of the input waveguide surface to the area of the resonator surface (a.r.=area of input waveguide surface/area of resonator surface). A large bandwidth corresponds to a small aspect ratio while a small bandwidth corresponds to a large aspect ratio. Correspondingly, a large bandwidth can be achieved by either increasing the area of the resonator surface, decreasing the area of the input waveguide surface, or adjusting both surface areas in such a manner to achieve a relatively small ratio number. A small bandwidth can be achieved by either decreasing the area of the resonator surface, increasing the area of the input waveguide surface, or adjusting both surface areas in such a manner to achieve a relatively large ratio number. Even further, increases or decreases of surface area can be achieved by adjusting one or both of the surface dimensions of the waveguide or resonator surfaces. For example, depth “D” of surface 119 or 123 may be increased or decreased according to desired bandwidth.

[0008] Since the resonator 122 and the input and output waveguides 118, 120 are formed together during the same process steps as described above, the depth, D, of the resonator is essentially fixed as the same depth of the waveguides and therefore the resonator bandwidth is fixed. Moreover, changes in depth that result in increased resonator bandwidth are not trivially accomplished and often result in complicated manufacturing processes and excessive resource and financial expenditures.

[0009] Accordingly, the thermo optic arts desire resonators having increased bandwidths that are relatively cheap and quick to produce without sacrifices in any resonator quality, reliability or longevity.

SUMMARY OF THE INVENTION

[0010] The above-mentioned and other problems become solved by applying the apparatus and method principles and teachings associated with the hereinafter described resonator for thermo optic device.

[0011] In one embodiment, the resonator of a thermo optic device is formed in the same process steps as a waveguide and is formed in a depression of a lower cladding while the waveguide is formed on a surface of the lower cladding. In this manner, since an upper surface of the resonator and the waveguide is substantially coplanar, the aspect ratio, as between the waveguide and resonator in an area where the waveguide and resonator front or face one another, decreases thereby increasing the bandwidth of the resonator. The depression is formed by photomasking and etching the lower cladding before forming the resonator and waveguide. Some depression embodiments include trenches, concavities and angular indentations.

[0012] In another embodiment, a plurality of resonators are taught that are formed in a plurality of depressions of the lower cladding while a plurality of waveguides are formed on the surface of the lower cladding.

[0013] In still another embodiment, waveguide(s) are formed in the depression(s) of the lower cladding while the resonator is formed on the surface. In this manner, the aspect ratio increases thereby decreasing bandwidth of the resonator.

[0014] Thermo optic devices formed with these resonators are also taught.

[0015] These and other embodiments, aspects, advantages, and features of the present invention will be set forth in part in the description which follows, and in part will become apparent to those skilled in the art by reference to the following description of the invention and referenced drawings or by practice of the invention. The aspects, advantages, and features of the invention are realized and attained by means of the instrumentalities, procedures, and combinations particularly pointed out in the appended claims.

BRIEF DESCRIPTION OF THE DRAWINGS

[0016]FIG. 1A is a cross sectional view of a thermo optic device in the form of an optical waveguide in accordance with the prior art;

[0017]FIG. 1B is a planar view of the thermo optic device of FIG. 1A;

[0018]FIG. 2A is a cross sectional view of a lower cladding in which a resonator in accordance with the teachings of the present invention will be formed;

[0019]FIG. 2B is a cross sectional view in accordance with the teachings of the present invention of a first photomasking step in a processing step subsequent to FIG. 2A;

[0020]FIG. 2C is a cross sectional view in accordance with the teachings of the present invention of a depression formed in a lower cladding in a processing step subsequent to FIG. 2B;

[0021]FIG. 2D is a cross sectional view in accordance with the teachings of the present invention of a layer deposited on the lower cladding in a processing step subsequent to FIG. 2C;

[0022]FIG. 2E is a cross sectional view in accordance with the teachings of the present invention of a second photomasking step in a processing step subsequent to FIG. 2D;

[0023]FIG. 2F is a cross sectional view in accordance with the teachings of the present invention of a patterned resonator and waveguides in a processing step subsequent to FIG. 2E;

[0024]FIG. 2G is a cross sectional view in accordance with the teachings of the present invention of a resonator and waveguides covered by an upper cladding thereby forming a thermo optic device in a processing step subsequent to FIG. 2F;

[0025]FIG. 3A is a cross sectional view in accordance with the teachings of the present invention of another embodiment of a depression in a lower cladding;

[0026]FIG. 3B is a cross sectional view in accordance with the teachings of the present invention of still another embodiment of a depression in a lower cladding;

[0027]FIG. 4A is a cross sectional view in accordance with the teachings of the present invention of an input waveguide formed in a depression of a lower cladding;

[0028]FIG. 4B is a cross sectional view in accordance with the teachings of the present invention of an input and output waveguide formed in depressions of a lower cladding;

[0029]FIG. 5 is a cross sectional view in accordance with the teachings of the present invention of a plurality of resonators formed in a plurality of depressions of a lower cladding;

[0030]FIG. 6 is a perspective view in accordance with the teachings of the present invention of a depression formed across a lower cladding;

[0031]FIG. 7 is a perspective view of an alternative embodiment of a plurality of depressions formed in a lower cladding;

[0032]FIG. 8 is a perspective view in accordance with the teachings of the present invention of a depression pattern formed in a lower cladding;

[0033]FIG. 9 is a perspective view in accordance with the teachings of the present invention of a plurality of regions of the lower cladding having depressions formed therein;

[0034]FIG. 10 is a cross sectional view in accordance with the teachings of the present invention of a waveguide and a resonator formed in a plurality of depressions of the lower cladding;

[0035]FIG. 11 is a block diagram of a system having a thermo optic package comprising resonators formed in accordance with the teachings of the present invention; and

[0036]FIG. 12 is an alternative embodiment of a thermo optic package comprising resonators formed in accordance with the teachings of the present invention.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0037] In the following detailed description of the preferred embodiments, reference is made to the accompanying drawings which form a part hereof, and in which is shown by way of illustration, specific embodiments in which the inventions may be practiced. These embodiments are described in sufficient detail to enable those skilled in the art to practice the invention, and it is to be understood that other embodiments may be utilized and that process, electrical or mechanical changes may be made without departing from the scope of the present invention. The term substrate used in this specification includes any base semiconductor structure such as silicon-on-sapphire (SOS) technology, silicon-on-insulator (SOI) technology, thin film transistor (TFT) technology, doped and undoped semiconductors, epitaxial layers of a silicon supported by a base semiconductor structure, as well as other semiconductor structures well known to one skilled in the art. The following detailed description is, therefore, not to be taken in a limiting sense, and the scope of the present invention is defined only by the appended claims and their equivalents.

[0038] The following description and figures use a reference numeral convention where the first digit of the reference numeral corresponds to the figure and the following two digits correspond to like elements throughout the specification. For example, the lower cladding of a thermo optic device of the present invention has a reference number of 202, 302, 402, etc. corresponding to the lower cladding X02 in FIGS. 2, 3, 4, etc. where X is the number of the figure in which the reference numeral appears.

[0039] With reference to FIG. 2A, a substrate 200 is provided upon which a resonator for use with a thermo optic device will be formed. In one embodiment the substrate is silicon. In another embodiment, it is a printed circuit board. In still another, it is any surface upon which a layer may be deposited.

[0040] A first layer 202 or lower cladding is formed on the substrate. In one embodiment, the substrate is some form of silicon and the first layer is formed as a grown layer via oxidation of the substrate. In another embodiment, the first layer is formed by deposition techniques.

[0041] Some particular deposition techniques for the first layer, and all remaining deposited layers, include, but are not limited to, any variety of chemical vapor depositions (CVD), physical vapor depositions (PVD), epitaxy, evaporation, sputtering or other known or hereinafter developed techniques. Specific CVD techniques include low pressure (LP) ones, but could also be atmospheric pressure (AP), plasma enhanced (PE), high density plasma (HDP) or other.

[0042] In one particular embodiment, the first layer is a silicon oxide that is deposited via a LPCVD technique using a tetraethyl orthosilicate or TEOS source.

[0043] After depositing the first layer, a first mask 204 is provided to photo impact 206 the first layer 202 in a photomasking step so that a photo impacted region 208 is formed in the lower cladding.

[0044] In one embodiment, the photo impacting is accomplished with an ultraviolet light from a photolithography device well known to those skilled in the art. The photo impacting, however, should not be limited to such an embodiment and may alternatively include X-rays or other light sources.

[0045] The first mask 204 may be configured as a clear-field or dark-field mask, as those terms as well understood by skilled artisans, according to the desired design of the photo impacted region 208 in the lower cladding.

[0046] Thereafter, with reference to FIG. 2C, the first layer 202 is etched so that the photo impacted region 208 is removed thereby leaving or forming a depression 210 in the lower cladding. In the embodiment shown, the depression 210 is shaped as a trench but it may also comprise other shapes, such as a concavity 310A (FIG. 3A), an angular indentation 310B (FIG. 3b) or other.

[0047] It should be appreciated that while the depression 210 is depicted in a cross sectional view it also has a lengthwise dimension (into or away from the paper) and it may be formed completely across the surface of the lower cladding or may be formed in just a particular region thereof. For example, with reference to FIG. 6, the depression is formed as a trench 610 across an entire surface 621 of lower cladding 602. In FIG. 7, the depression is formed as a plurality of concavities 710 in only various regions of surface 721 of lower cladding 702.

[0048] In still another embodiment, the depression may take on a desired pattern or shape across the lower cladding or in just a particular region. For example, in FIG. 8, the depression is formed as a trench 810 extending lengthwise across surface 821 of the lower cladding 802. The trench 810 has a bend 811 representative of at least one depression pattern. In FIG. 9, the depression of the lower cladding 902 is represented as a plurality of concavities 910 having a generally cube shape that is formed in various specific or random regions of surface 921.

[0049] Those skilled in the art will appreciate that even further forms, shapes and dimensions of depressions are formable in the lower cladding and include, but are not limited to rectangles, circles, serpentine formations, tooth-shaped patterns, polygons, triangles, squares, or any other geometric shape(s) that could be fabricated with the first mask. It should be further appreciated that the particularly shown trenches, concavities, and angular indentations may be of various dimensions and take on any or all embodiments shown herein.

[0050] With reference to FIGS. 2B and 2C, some etching techniques embraced by this invention for removing the photo impacted region 208 from the lower cladding 202 to form depression 210 include, but are not limited to, any variety of wet etches including immersion or spray, or dry etches including plasma, barrel or planar, ion milling, reactive ion etches (RIE) or deep RIE.

[0051] In one particular embodiment of the invention, the photo impacted region 208 is dry etched with a photo resist pattern and CF₄ or CF₄CHF₃ Argon based chemistry in a parallel plate reactor for 360 seconds under the conditions of about 50 militorr, 600 watts and 13.56 MHz.

[0052] With reference to FIG. 2D, a second layer 212 is formed on the surface of the first layer 202 in such a manner to “fill” the depression 210 and cover the lower cladding as shown.

[0053] In one embodiment, the second layer is a silicon oxynitride deposited with a PECVD technique using a silane with nitrous oxide reaction in an argon or helium plasma for 180 seconds, under the conditions of 400° C., 450 watts and 13.56 MHz. In another embodiment, the second layer is a translucent material.

[0054] While the lower cladding, in one embodiment, was formed of a silicon oxide and the second layer was formed of silicon oxynitride, it should be appreciated that numerous other materials for these first and second layers exist. What dictates the selection of the materials is the index of refraction. This is because the second layer will be formed into the waveguide and resonator and light will be propagated therein via reflections of light that occur at the boundary where the two layers meet. So long as the second layer is a material having an index of refraction that is different, either higher or lower, than the index of refraction for the first layer (at whatever wavelength of light the thermo optic device is designed for) light signals can be propagated.

[0055] With reference to FIG. 2E, after depositing the second layer 212, a second mask 214 is provided to photo impact 216 the second layer 212 in another photomasking step.

[0056] As with the first photomasking step, the photo impacting is accomplished with an ultraviolet light from a photolithography device but may alternatively include X-rays or other light sources. The second mask be configured in such a way that the photo impacted region of the second layer takes on a desired form such as those previously shown. Some particular mask embodiments include, but are not limited to, clear-field or dark-field masks.

[0057] As shown in FIG. 2F, the photo impacted region 209 of the second layer 212 caused by photo impacting 216 is etched away thereby forming a resonator 222 and at least one waveguide. In this embodiment, the waveguide is an optical waveguide having an input waveguide 218 and an output waveguide 220 on either sides of the resonator.

[0058] Many things should now be apparent to those skilled in the art. For example, the resonator 222 has a portion thereof, having a depth “D,” formed in the depression between surface 221 of first layer 202 and depression bottom 223. It has another portion thereof formed between surface 221 and plane 225. Simultaneously, the waveguides 218, 220 have no portion thereof formed in the depression and all portions thereof formed on the surface 221 of the first layer and extending from the surface 221 to plane 225. As a result, the aspect ratio between the resonator and the waveguides has decreased (in comparison to the prior art, FIG. 1A, for example) thereby increasing resonator bandwidth.

[0059] In particular, the aspect ratio (a.r.) in area 231 has decreased where the input waveguide 218 and resonator 222 front one another along resonator surface 223 and input waveguide surface 219, wherein (a.r.) in area 231 is defined as the area of the input waveguide surface 219 to the area of the resonator surface 223 or (a.r.=area of input waveguide surface 219/area of resonator surface 223). (As will become apparent from the following discussion, the aspect ratio between adjacent resonators (FIG. 5, 522A and 522B) also decreases which also helps with easier processing for the top cladding layer.)

[0060] In area 233, the aspect ratio has similarly decreased where the output waveguide 220 and resonator 222 front one another along resonator surface 225 and output waveguide surface 221, wherein (a.r.) in area 233 is defined as the area of the output waveguide surface 221 to the area of the resonator surface 225 or (a.r.=area of output waveguide surface 221/area of resonator surface 225).

[0061] In one particular embodiment of the invention, it has been discovered that the aspect ratio decreased so significantly that the resonator bandwidth approximately doubled by increasing from about 16 nm to about 32 nm.

[0062] The depth “d” to which the resonator is formed in or fills the depression is dictated by at least two factors. The first is a practical limitation governed by the fill capability inherent in the material of the second layer. For example, if the second layer were deposited as a liquid (amorphous), and the depth of the depression was a relatively substantial percentage of the thickness of the lower cladding, it would likely fill to a greater depth than a non-liquid. Second, the depth is a function of the frequency gain the designed resonator is trying to achieve and varies greatly from application to application.

[0063] The height of the resonator between surface 221 and plane 225 is not required to be any particular height and is dictated according to the frequency characteristics demanded by the particular application in which the resonator is used. As a reference point, however, resonator and waveguide height is often in a range from about 1 to about 2 microns.

[0064] Similarly, the horizontal spacing between the resonators and the waveguides is not required to be any particular distance and is dictated according to the frequency characteristics demanded by the particular application in which the resonator is used. As a reference point, however, horizontal spacing between resonators and waveguides is often in a range from about 1 to about 2 microns.

[0065] It should also be appreciated that the upper surfaces of the input and output waveguides 218, 220 and resonator 222 are all substantially coplanar as defined by plane 225 (although only shown in one dimension). As a result, the manufacturing of a resonator having an increased bandwidth is completed after the etching process performed on the second layer and no additional processing steps need to occur.

[0066] To complete the thermo optic device, however, a third layer 224 or upper cladding is deposited on the waveguides 218, 220, the resonator 222 and portions 235 of the lower cladding not having a waveguide or resonator. The upper cladding is deposited to a thickness sufficient to prevent outside light from interfering with the light propagated in the waveguide during use. As a reference point, however, thickness for both the upper and lower claddings is often the same and in one embodiment is about 4 microns nominally.

[0067] In one embodiment, the third layer is a second silicon oxide layer deposited in the same manner as previously described for the first layer. In another embodiment, the third layer has an index of refraction that is substantially equal to the index of refraction of the first layer.

[0068] It will be appreciated that the third layer 224 has an upper surface 226 that can be used to stack multiple thermo optic devices by continuing the deposition, patterning and etching processes described herein. The surface 226 may alternatively contain a heater (not shown) for changing a thermo optical property of the device as light propagates in the waveguide during use.

[0069] With reference to FIG. 5, it will be appreciated that thermo optic devices of the present invention may be formed with a more than a single resonator. For example, a plurality of resonators, first and second resonators 522A and 522B, are formed in a corresponding number of depressions, first and second depressions 510A and 510B, while first and second waveguides, input and output waveguides 518, 520 are formed on the surface 521 of the lower cladding. In one embodiment, the horizontal spacing between adjacent resonators is in a range from about 2 to about 3 microns while the horizontal width of the resonator is about 2 microns nominally. In this manner, even further variations in the frequency characteristics of the resonator can be achieved as application demand varies.

[0070] Those skilled in the art will appreciate that still other numbers of resonators could be formed in the depressions while forming waveguides on the surface of the lower cladding.

[0071] While the foregoing teaches resonators having increased bandwidth, in an alternate embodiment of the present invention, it may be desirable to decrease resonator bandwidth by increasing the previously described aspect ratio(s).

[0072] For example, with reference to FIG. 4A, a first waveguide, input waveguide 418A is formed in a depression 410 while resonator 422 is formed on the surface 421 of the lower cladding 402. In FIG. 4B, a first and second waveguide, input and output waveguides 418B, 420B are formed in depressions 410 while the resonator 422 is formed on surface 421 of the lower cladding 402.

[0073] In still another embodiment, it may be desirable to increase some resonator bandwidths while decreasing others. With reference to FIG. 10, waveguide 1018 is formed in a first depression 1010A while a first resonator, resonator 1022A, is formed on the surface 1021 of the lower cladding 1002. Accordingly, the aspect ratio in area 1031 is increased as between waveguide 1018 and resonator 1022A, thereby decreasing bandwidth of resonator 1022A. Waveguide 1020, on the other hand, is formed on the surface 1021 while a second resonator, resonator 1022B, is formed in depression 1010B of the lower cladding. Accordingly, the aspect ratio in area 1033 is decreased as between waveguide 1022 and resonator 1022B, thereby increasing bandwidth of resonator 1022B.

[0074] It will be appreciated that during use, the resonators of the present invention may be used with thermo optic devices in a variety of applications. For example, the thermo optic device may be an amplifier, modulator, gate, filter, time delay element, switch, multiplexer, or other.

[0075] With reference to FIG. 11, a system, having as part thereof a resonator or waveguide formed in accordance with the teachings of the present invention, is shown generally as 1141. The system may be an exclusively fiber optic system or may be a system having other software and hardware devices, as indicated by the dashed line 1145, operably coupled to at least one fiber optic component thereof.

[0076] In either system, a light source 1143 will be provided as the source for propagating light signals along at least one fiber optic line 1147. Well known light sources include, but are not limited to, laser light sources. In the embodiment shown, the system 1141 includes a plurality of fiber optic lines 1147.

[0077] Coupleable to the fiber optic lines via a plurality of input fiber optic ports 1151 is a thermo optic package 1149. Contained within the thermo optic package is at least one thermo optic device 1153 having at least one resonator or waveguide formed in accordance with the present invention. In the embodiment shown, the thermo optic device 1153 is coupled to the input fiber optic port 1151 via an input connector 1155 while an output connector 1157 couples the thermo optic device to an output fiber optic port 1159. In turn, the output fiber optic port 1159 is coupled to another fiber optic line 1147 of system 1141.

[0078] During use, a system user merely needs to couple fiber optic lines 1147 to the input and output fiber optic ports of the package 1149 to readily achieve at least one resonator or waveguide having an increased or decreased bandwidth as necessary.

[0079] With reference to FIG. 12, an alternative embodiment of a thermo optic package 1249 is shown having a thermo optic device 1253 with a single input connector 1255 and a plurality of output connectors 1257. The input connector 1255 connects with input fiber optic port 1251 which is readily matable with a fiber optic line 1247 of a system. The output connectors 1257 of thermo optic device 1253 are each matable with an output fiber optic port 1259.

[0080] In another embodiment, the single input connector of the thermo optic device 1253, having a resonator or waveguide formed in accordance with the present invention, may alternatively be replaced with two or more input connectors while the two output connectors may be replaced with one or more output connectors depending upon the type and desired use of the thermo optic device 1253.

Conclusion

[0081] The above structures and fabrication methods have been described, by way of example, and not by way of limitation, with respect to resonators for thermo optic devices.

[0082] In particular, the resonator of a thermo optic device is formed in the same process steps as a waveguide and is formed in a depression of a lower cladding while the waveguide is formed on a surface of the lower cladding. In this manner, since an upper surface of the resonator and the waveguide is substantially coplanar, the aspect ratio as between the waveguide and resonator in an area where the waveguide and resonator front or face one another decreases thereby increasing the bandwidth of the resonator. The depression is formed by photomasking and etching the lower cladding before forming the resonator and waveguide. Some depression embodiments include trenches, concavities and angular indentations.

[0083] In another embodiment, a plurality of resonators are taught that are formed in a plurality of depressions of the lower cladding while a plurality of waveguides are formed on the surface of the lower cladding.

[0084] In still another embodiment, waveguide(s) are formed in the depression(s) of the lower cladding while the resonator is formed on the surface. In this manner, the aspect ratio increases thereby decreasing bandwidth of the resonator.

[0085] Thermo optic devices formed with these resonators are also taught.

[0086] As a result, resonators of this invention can be formed quicker and cheaper without any corresponding sacrifice in quality, reliability or longevity.

[0087] The present invention has been particularly shown and described with respect to certain preferred embodiment(s). However, it will be readily apparent to those of ordinary skill in the art that a wide variety of alternate embodiments, adaptations or variations of the preferred embodiment(s), and/or equivalent embodiments may be made without departing from the intended scope of the present invention as set forth in the appended claims. Accordingly, the present invention is not limited except as by the appended claims. 

What is claimed is:
 1. A method, comprising: forming a lower cladding; forming a depression in the lower cladding; and forming a resonator in the depression.
 2. The method according to claim 1, further including forming a waveguide on a surface of the lower cladding.
 3. The method according to claim 1, further including forming an upper cladding over the resonator.
 4. The method according to claim 1, wherein the forming the depression further includes photomasking the lower cladding.
 5. The method according to claim 2, wherein the forming the depression further includes etching a photo impacted region of the lower cladding.
 6. A method, comprising: providing a substrate; forming a lower cladding on the substrate, the lower cladding having a surface; forming a depression in the lower cladding; forming a resonator in the depression; and forming a waveguide on the surface.
 7. The method according to claim 6, wherein the forming the lower cladding further includes one of depositing a silicon oxide and oxidizing the substrate.
 8. The method according to claim 6, wherein the forming the resonator further includes depositing a silicon oxynitride.
 9. The method according to claim 8, wherein the forming the resonator further includes photomasking the silicon oxynitride.
 10. The method according to claim 9, wherein the forming the resonator further includes etching the silicon oxynitride.
 11. A method, comprising: forming a lower cladding having a surface; forming a plurality of depressions in the lower cladding; and forming a plurality of resonators in the plurality of depressions.
 12. The method according to claim 11, further including forming a waveguide on the surface of the lower cladding.
 13. The method according to claim 11, further including forming an upper cladding over the plurality of resonators.
 14. The method according to claim 11, wherein the forming the depression further includes photomasking the lower cladding.
 15. The method according to claim 14, wherein the forming the depression further includes etching a photo impacted region of the lower cladding.
 16. A method, comprising: providing a substrate; forming a lower cladding on the substrate, the lower cladding having a surface; forming a depression in the lower cladding; forming one of a first resonator and a first waveguide in the depression; and forming one of a second resonator and a second waveguide on the surface.
 17. The method according to claim 16, wherein the forming the depression in the lower cladding further includes one of forming a trench, forming a concavity, and forming an angular indentation.
 18. The method according to claim 16, wherein the forming the one of the first resonator and the first waveguide further includes depositing a layer on the surface and over the depression.
 19. The method according to claim 18, wherein the forming the one of the first resonator and the first waveguide further includes photomasking the layer.
 20. The method according to claim 19, wherein the forming the one of the first resonator and the first waveguide further includes etching the layer.
 21. A method, comprising: providing a substrate; forming a lower cladding on the substrate, the lower cladding having a surface; forming a first trench in the lower cladding; forming a first resonator in the trench; forming a first waveguide on the surface wherein the first waveguide and the first resonator have an upper surface that is substantially coplanar; and forming an upper cladding over the first resonator and the first waveguide.
 22. The method according to claim 21, further including forming a second trench in the lower cladding.
 23. The method according to claim 22, further including forming a second resonator in the second trench.
 24. The method according to claim 21, further including forming a second waveguide on the surface.
 25. A method, comprising: providing a substrate; forming a lower cladding on the substrate, the lower cladding having a surface; forming a plurality of trenches in the lower cladding; forming a plurality of resonators in the plurality of trenches; forming a plurality of waveguides on the surface wherein the plurality of waveguides and the plurality of resonators each have an upper surface that is substantially coplanar; and forming an upper cladding over the plurality of resonators and the plurality of waveguides.
 26. The method according to claim 25, wherein the forming the lower cladding further includes one of depositing a silicon oxide and oxidizing the substrate.
 27. The method according to claim 25, wherein the forming the resonator further includes depositing a silicon oxynitride.
 28. The method according to claim 27, wherein the forming the resonator further includes photomasking the silicon oxynitride.
 29. The method according to claim 28, wherein the forming the resonator further includes etching the silicon oxynitride.
 30. A method, comprising: providing a substrate; depositing a first layer on the substrate, the first layer having a surface; photomasking the first layer; etching the first layer to form a trench in the first layer; depositing a second layer over the first layer and the trench; photomasking the second layer; etching the second layer to form a resonator in the trench and an input and output waveguide on the surface wherein the resonator and the input and output waveguides each have an upper surface that is substantially coplanar; and depositing a third layer over the resonator and the input and output waveguides to form a thermo optic device.
 31. The method according to claim 30, further including selecting the first and third layers to have an index of refraction that is substantially equal.
 32. The method according to claim 31, further including selecting the second layer to have an index of refraction that is substantially different than the substantially equal index of refraction for the first and the third layers.
 33. A method, comprising: providing a silicon substrate; depositing a first silicon oxide on the silicon substrate, the first silicon oxide having a surface; photomasking the first silicon oxide; etching the first silicon oxide to form a trench therein; depositing a silicon oxynitride over the first silicon oxide and the trench; photomasking the silicon oxynitride; etching the silicon oxynitride to form a resonator in the trench and an input and output waveguide on the surface wherein the resonator and the input and output waveguides each have an upper surface that is substantially coplanar; and depositing a second silicon oxide over the resonator and the input and output waveguides to form a thermo optical waveguide, wherein the first and second silicon oxides have an index of refraction that is substantially equal and the silicon oxynitride has an index of refraction that is substantially different than the substantially equal index of refraction for the first and second silicon oxides.
 34. An apparatus formed in accordance with the method of claim
 33. 35. An apparatus, comprising: a lower cladding having a depression therein; and a portion of a resonator in the depression.
 36. The apparatus according to claim 35, further including a waveguide on a surface of the lower cladding.
 37. The apparatus according to claim 35, further including an upper cladding on the resonator.
 38. The apparatus according to claim 35, wherein the depression is one of a trench, a concavity and an angular indentation.
 39. An apparatus, comprising: a substrate a lower cladding on the substrate having a depression and a surface; and a resonator in the depression.
 40. The apparatus according to claim 39, further including an input and output waveguide on the surface.
 41. The apparatus according to claim 40, wherein the resonator and the input and output waveguides have an upper surface that is substantially coplanar.
 42. The apparatus according to claim 35, wherein the resonator and the lower cladding are formed of materials having different indices of refraction.
 43. A thermo optic device, comprising: a lower cladding having a trench and a surface; a resonator in the trench; and a waveguide on the surface.
 44. The thermo optic device according to claim 43, further including a substrate, the lower cladding being on the substrate.
 45. The thermo optic device according to claim 44, wherein the waveguide includes an input and output waveguide.
 46. The thermo optic device according to claim 45, further including an upper cladding on the resonator and the input and output waveguides.
 47. An apparatus, comprising: a lower cladding having a surface and a plurality of depressions therein; and a plurality of resonators in the plurality of depressions, the plurality of depressions being equal in number to the plurality of resonators.
 48. The apparatus according to claim 47, further including a plurality of waveguides on the surface.
 49. The apparatus according to claim 48, wherein an upper surface of each of the plurality of waveguides and the plurality of resonators is substantially coplanar.
 50. The apparatus according to claim 48, further including an upper cladding on the plurality of resonators and the plurality of waveguides.
 51. The apparatus according to claim 47, wherein one of the plurality of depressions is one of a trench, a concavity and an angular indentation.
 52. A thermo optic device, comprising: a substrate; a lower cladding on the substrate having a depression therein and a surface; one of a resonator and a waveguide in the depression and the other of the resonator and the waveguide on the surface wherein an upper surface of each of the resonator and the waveguide is substantially coplanar; and an upper cladding on the resonator and the waveguide.
 53. The thermo optic device according to claim 52, wherein the resonator and the waveguide are substantially the same material.
 54. The thermo optic device according to claim 52, wherein the upper cladding and the lower cladding are substantially the same material.
 55. A thermo optical waveguide, comprising: a substrate; a lower cladding on the substrate having a plurality of depressions therein and a surface; a plurality of resonators in the plurality of depressions, the plurality of depressions being equal in number to the plurality of resonators; an input and output waveguide on the surface wherein an upper surface of each of the plurality of resonators and the input and output waveguides is substantially coplanar; and an upper cladding on the plurality of resonators and the input and output waveguides.
 56. The thermo optical waveguide according to claim 55, wherein one of the plurality of depressions is one of a trench, a concavity and an angular indentation.
 57. A thermo optic device, comprising: a substrate; a first layer on the substrate, the first layer having a depression therein and a surface; a second layer, a first portion of the second layer in the depression; a third layer on a second portion of the second layer and on the surface of the first layer wherein the first and second layers each have an index of refraction that is substantially equal to one another, wherein the second layer has an index of refraction that is one of substantially higher and substantially lower than the substantially equal indices of refraction for the first and second layers.
 58. A thermo optical waveguide, comprising: a substrate; a lower cladding on the substrate having a plurality of trenches therein and a surface; a plurality of resonators in the plurality of trenches, the plurality of trenches being equal in number to the plurality of resonators; an input and output waveguide on the surface wherein an upper surface of each of the plurality of resonators and the input and output waveguides is substantially coplanar; and an upper cladding on the plurality of resonators and the input and output waveguides wherein the upper and lower cladding each have an index of refraction that is substantially equal to one another, wherein the plurality of resonators and input and output waveguides each have an index of refraction that is one of substantially higher and substantially lower than the substantially equal indices of refraction for the upper and lower cladding.
 59. A thermo optical waveguide, comprising: a silicon substrate; a first silicon oxide on the substrate having a plurality of trenches therein and a surface; a plurality of resonators in the plurality of trenches formed of a silicon oxynitride, the plurality of trenches being equal in number to the plurality of resonators; an input and output waveguide on the surface formed of a silicon oxynitride wherein an upper surface of each of the plurality of resonators and the input and output waveguides is substantially coplanar; and a second silicon oxide on the plurality of resonators and the input and output waveguides wherein the first and second silicon oxides each have an index of refraction that is substantially equal to one another, wherein the plurality of resonators and input and output waveguides each have an index of refraction that is substantially equal to one another and one of substantially higher and substantially lower than the substantially equal indices of refraction for the first and second silicon oxide.
 60. A system having a fiber optic line, comprising: a thermo optic package coupleable with the fiber optic line; and a thermo optic device in the thermo optic package having a lower cladding having a depression and a surface; a resonator in the depression; and a waveguide on the surface.
 61. The system of claim 60, wherein the thermo optic package further includes at least one input fiber optic port and at least one output fiber optic port.
 62. The system of claim 61, wherein the thermo optic device includes at least one input connector coupled to the at least one input fiber optic port and at least one output connector coupled to the at least one output fiber optic port.
 63. A thermo optic package, comprising: a thermo optic device having: i) a lower cladding having a depression and a surface; ii) a resonator in the depression; and iii) a waveguide on the surface.
 64. The thermo optic package according to claim 63, further including an input connector and an output connector coupled with the thermo optic device.
 65. The thermo optic package according to claim 64, further including an input fiber optic port coupled to the input connector and an output fiber optic port coupled to the output connector. 